Galvanic Series of some commercial Metals and Alloys in Seawater

The Table is based on potential measurements and galvanic corrosion tests performed by The International Nickel Company at Harbour Island, North Carolina, in unpolluted seawater.

The relative placements of metals, rather than their potentials, are provided due to variances between the tests. Similar series should be conducted for metals and alloys in all conditions and at all temperatures, but this would necessitate nearly endless testing.

Stainless steels occupy a more noble position when they are in a passive state as opposed to a less noble position when they are in an active state. Inconel, which can be thought of as a stainless nickel, exhibits behaviour similar to that of nickel. The brackets in Table 3-2 are another intriguing aspect of the galvanic series. The alloys included in these brackets have a base composition that is somewhat similar, such as copper and copper alloys. The bracket shows that when metals in a certain bracket are linked or in contact with one another, there is typically a low risk of galvanic corrosion. This is due to the series’ close proximity of these components and the low potential of the couples they produce. The potential created increases with the series distance.

In simple terms, we observe an increase in nobility or cathodicity of the materials as we ascend the galvanic series table, relative to those that are located lower, which are characterized by higher activity or anodicity. Take, for instance, Nickel and Lead in a scenario where they are in contact under humid conditions. Due to Lead’s elevated activity, it would be susceptible to preferential corrosion by means of the galvanic corrosion mechanism. It’s important to note that the facilitation of galvanic corrosion requires the presence of both a potential difference between the materials and an electrolytic medium.

Anil K Vashishta

Anil K Vashishta is a Metallurgical Engineer from the National Institute of Technology, Rourkela, with over 29 years of expertise in materials, corrosion, and metallurgical/mechanical laboratory management. As the Managing Director of Colossal Consultants LLC in the United Arab Emirates—founded in 2019 to serve the GCC and South-Eastern regions—Anil applies his extensive background to support diverse industries, particularly oil and gas.
A Certified NACE Corrosion Specialist and NACE Material Selection Design Specialist, Anil specializes in corrosion assessment and mitigation, material selection, turnkey laboratory setup, and root cause/failure analysis. His comprehensive skills also include in-situ replica metallography, condition assessment, coating evaluations, and cathodic protection. With a deep passion for technical excellence and practical solutions, Anil continues to drive innovation and best practices in the field of materials engineering.

In this article

Macro features
Macroscopic Features of Different Failure Modes
HFE
Human Factors Engineering: Designing Workplaces for People
IMG_1605349140213
Coating Deterioration Assessment of a High-Rise Steel Structure in Baku
Thinning
Root Cause Analysis of Heat Exchanger Tube Failures
Galvanic Corrosion
Understanding Galvanic Corrosion: Causes, Effects, and Prevention
HIC crack
Hydrogen Induced Cracking in Boiler Water Drum Manway Neck Weld
hi8
Corrosion Under Insulation (CUI) at a Dubai Hotel Swimming Pool
creep-rupture-testing-machine-250x250
Elevated temperature Creep test of Metallic Material
Fracture
Fractography
QRA
Quantitative Risk Assessment (QRA) using API 581
Scroll to Top
×