Erosion of Pipelines/Piping

Pipeline erosion and fluid flow velocity are well-known to be related. A fluid that is flowing through a pipeline applies force to the pipe’s inside surface. Erosion, also known as the wear away of the pipe material over time, can be brought on by this force. The amount of erosion that takes place is significantly influenced by the fluid’s velocity.

At low velocities, erosion is often not a big concern because the force the fluid exerts on the pipe is relatively minimal. Yet, the force acting on the pipe rises as the fluid’s velocity does. If the velocity is high enough, it may seriously harm the pipeline by causing erosion to happen more quickly.

The precise relationship between fluid velocity and erosion is determined by a number of factors, including fluid properties (such as viscosity and density), pipeline size and shape, and pipe material properties. Higher fluid velocities, on the other hand, result in faster erosion rates.

The optimum fluid flow velocity in pipelines to prevent erosion is determined by several factors, including fluid properties, pipeline size and shape, and pipe material. However, the maximum fluid flow velocity recommended to prevent erosion in pipelines is typically around 5 m/s (16.4 ft/s) for liquids and 30 m/s (98.4 ft/s) for gases.

If the fluid flow velocity exceeds these recommended limits, erosion can occur at a faster rate, causing pipeline damage. High fluid velocities can also cause turbulence, pressure drops, and increased pumping costs, in addition to erosion.

Engineers may use a variety of techniques to prevent pipeline erosion, such as selecting more resistant materials, modifying the shape of the pipeline to reduce fluid velocity, or using coatings or liners to protect the pipe surface.

Engineers use various methods such as flow modeling and analysis, pipeline design modifications, and flow control devices such as valves and flow restrictors to ensure that fluid flow velocities are within the recommended limits. They also choose pipeline materials that are resistant to erosion and corrosion, and they conduct routine maintenance and inspections to detect and address any erosion-related issues.

Anil K Vashishta

Anil K Vashishta is a Metallurgical Engineer from the National Institute of Technology, Rourkela, with over 29 years of expertise in materials, corrosion, and metallurgical/mechanical laboratory management. As the Managing Director of Colossal Consultants LLC in the United Arab Emirates—founded in 2019 to serve the GCC and South-Eastern regions—Anil applies his extensive background to support diverse industries, particularly oil and gas.
A Certified NACE Corrosion Specialist and NACE Material Selection Design Specialist, Anil specializes in corrosion assessment and mitigation, material selection, turnkey laboratory setup, and root cause/failure analysis. His comprehensive skills also include in-situ replica metallography, condition assessment, coating evaluations, and cathodic protection. With a deep passion for technical excellence and practical solutions, Anil continues to drive innovation and best practices in the field of materials engineering.

In this article

Macro features
Macroscopic Features of Different Failure Modes
HFE
Human Factors Engineering: Designing Workplaces for People
IMG_1605349140213
Coating Deterioration Assessment of a High-Rise Steel Structure in Baku
Thinning
Root Cause Analysis of Heat Exchanger Tube Failures
Galvanic Corrosion
Understanding Galvanic Corrosion: Causes, Effects, and Prevention
HIC crack
Hydrogen Induced Cracking in Boiler Water Drum Manway Neck Weld
hi8
Corrosion Under Insulation (CUI) at a Dubai Hotel Swimming Pool
creep-rupture-testing-machine-250x250
Elevated temperature Creep test of Metallic Material
Fracture
Fractography
QRA
Quantitative Risk Assessment (QRA) using API 581
Scroll to Top
×